Synthesis and Photocatalytic Activity of Nano sized TiO2-30wt.%SrO Composite Powders
초록
영어
Nano-sized TiO2-30wt% SrO composite powders were synthesized by a sol-gel method. The
as-received amorphous TiO2-30wt% SrO composite powders were crystallized with anatase TiO2 at around 750 oC. As calcination temperatures increased, the anatase TiO2 crystalline phase was transformed to rutile TiO2 at about 900 oC, whereas SrTiO3 phase was detected. The peaks obtained after calcining at 1050 oC mainly exhibited the rutile TiO2 and SrTiO3 phases. For the comparison of photocatalytic activity depending on calcination temperatures, TiO2-30wt%SrO composite powders were tested in phenol degradation. TiO2-30wt% composite powder showed a good photoactivity for the photo- oxidation of phenol.
한국어
나노크기를 갖는 TiO2-30wt% SrO 복합분체는 졸-겔법을 이용하여 합성하였다. 합성된 무정형의
TiO2-30wt% SrO 복합분체는 750 oC에서 아나타제-TiO2로 결정화되었다. 하소 온도를 증가시킴에 따라아나타제-TiO2 결정상은 900 oC에서 루타일-TiO2로 상변태 하였으나 SrTiO3 상이 측정되었다. 1050 oC에서 하소한 후 얻어진 피이크는 주상으로 루타일-TiO2와 SrTiO3 상으로 나타났다. 하소온도에 따른 광촉매 효율을 측정하기 위해서 페놀의 감소율을 TiO2-30wt% SrO 복합분체로 측정하였다. TiO2-30wt% SrO 복합분체는 페놀의 광산화반응에 의해서 우수한 광촉매 효율을 보였다.
목차
Abstract
I. 서론
II. 실험 방법
II-I 분말 합성
II-II. 촉매활성 및 물성평가
III. 결과 및 고찰
IV. 결론
V. 참고문헌