Microstructure and Mechanical Properties of Hot Pressed Al2O3-Ni-P Nano-composites
초록
영어
Al2O3-Ni-P nano-composite powders with Ni-P contents of 10.9, 14.4 and 20.4 wt% were synthesized by Ni-P electroless deposition process. The as-received Al2O3-Ni-P composite powders were comprised of Ni-P particles and Ni-P coating layer. Some Ni-P particles were randomly adhered on the Al2O3 powders and theirs distribution of particle size was the range from 5nm to 20nm in diameter. The thin layer of Ni-P had an amorphous structure of about 5nm in thickness and was directly bonded with the Al2O3 powders. Using the Ni-P coated Al2O3 powders, densed Al2O3-Ni-P nano composite can be successfully obtained by the hot press process at 1350 oC for 1hour in an Ar atmosphere under an applied pressure of 30MPa. Hot pressed Al2O3-15wt% Ni-P nano composite showed excellent material properties among them. The values of relative density, Vickers hardness and fracture toughness were comparatively high value with about 99.1%, 2360 Hv and 6MPa.m1/2, respectively.
한국어
10.9, 14.4, 20.4wt% Ni-P 함유량을 갖는 Al2O3-Ni-P 나노복합체를 Ni-P 무전해도금 공정을 이용하여 합성하였다. As-received Al2O3-Ni-P 복합분체는 Ni-P 코팅층과 Ni-P 입자로 구성되었다. Ni-P 입자는 불규칙적으로 Al2O3 분말에 흡착되어 있으며 5-20nm의 직경을 갖는 입자 크기 분포를 갖는다. Ni-P 코팅층은 5nm의 두께를 갖는 무정형의 구조를 보이고 Al2O3 분말과 직접적으로 결합되어있다. Ni-P 코팅된 Al2O3 분말를 이용하여 1350 oC, 30MPa에서 1시간 동안 hot press 공정를 이용하여 치밀한 Al2O3-Ni-P 나노복합체를 성공적으로 얻었다. Hot pressed Al2O3-15wt% Ni-P 복합체는 매우 우수한 기계적 성질을 나타내었다. 상대밀도, Vickers 경도, 파괴인성은 각각 99.1%, 2360 Hv와 6MPa.m1/2 이었다.
목차
Abstract
I. 서론
II. 실험방법
III. 실험결과와 고찰
IV. 결론
V. 참고문헌