earticle

영어

Attempt was made to establish identification methods for irradiated starch. Commercial starches (corn starch/CS, sweet potato starch/SS, and potato starch/PS) were irradiated at 0-6.0 kGy and used to measure viscosity with Brookfield DV-III programmable rheometer. Starch suspensions were prepared at 8.0 (7.2%, d.b.), 8.5 (7.3%, d.b.), and 9.0% (7.3%, d.b.) for CS, SS, and PS, respectively at 100 rpm in spindle speed. Results showed viscosities of samples significantly decreased (pR2 0.9754, 0.9618, and 0.9888 for CS, SS, and PS, respectively. Irradiation dose at 1.5 kGy induced decrease in viscosity as compared to non-irradiated control by 34, 57, and 51% in CS, SS, and PS, respectively, suggesting viscometry could lie applied to identify irradiated starches. Solubility and alkali number of irradiated starches significantly increased with irradiation doses, while swelling power decreased (p<0.05). Results suggested solubility, alkali number, and swelling power for irradiated starches complement identification results of viscometry.

한국어

방사선 조사 전분류의 확인방법 연구의 일환으로 0, 1.5, 3.0, 4.5 및 6.0 kGy의 감마선을 조사한 옥수수 전분, 고구마 전분 및 감자 전분을 대상으로 일정 조건에서 조사선량별 점도를 Brookfield DV-III programmable rheometer를 사용하여 측정하였다. 전분 현탁액의 농도를 옥수수 전분 8.0%(건물량 7.2%), 고구마 전분 8.5%(건물량 7.3%) 및 감자 전분 9.0%(건물량 7.3%)로 조제하여 100rpm에서 점도를 측정한 결과, 모든 시료에서 조사선량이 증가함에 따라 점도가 유의적으로 감소하였고 (pR2 0.9754, 0.9618 및 0.9888의 높은 상관성이 확인되었다. 또한 1.5 kGy 조사선량에서도 옥수수 전분 34%, 고구마 전분 57%, 감자전분 51%의 점도 감소가 일어나 저선량 조사의 경우에도 뚜렷한 점도 변화가 관찰되어 방사선 조사 전분류의 확인방법으로써 적용 가능성이 높은 것으로 나타났다. 점도 측정에 의한 조사여부 판별의 신뢰도를 높일 수 있는 보조적인 확인 marker로써 용해도, 팽윤력, 청가 및 알칼리수를 검토한 결과, 조사선량이 증가함에 따라 용해도 및 알칼리수는 유의적으로 증가(p<0.05)한 반면, 팽윤력은 유의적으로 감소(p<0.05)하는 경향이 확인되었다.