earticle

영어

Mixing' and 'immersion' CaCl2 treatment methods were tested for preparation of bio-degradable films using powders of sea mustard (Undaria pinnatifida) (leaf, stem, and sphorophyll), sweet tanlge (Laminaria japonica), and fusiforme (Hizikia fusiforme) by extracting alginate through acid-alkali extraction method. Except fusiforme powder, flexible, free-standing films were produced by both methods using all marine algae powders tested. Except water solubility (WS), surface color, tensile strength (TS), elongation at break (E), and water vapor permeability (WVP) did not show distinct difference between CaCl2, treatment methods. Although TS, WVP, and WS of marine algae powder films were lower than those of alginate films, they indicate potential in application as a new source of bio-degradable packaging materials.

한국어

해조분말을 이용하여 산 알칼리 병용법으로 알긴산을 추출하고 필름의 물성 증진을 위하여 두 가지의 CaCl2 처리방법 (즉, CaCl2를 필름용액에 직접 첨가하는 방법과 필름을 제조한 후 필름을 CaCl2, 용액에 침지하여 가교결합을 유도하는 방법)을 적용하여 생분해성 필름을 제조하고 그 물성을 비교하였다. 사용된 해조분말(미역 잎, 미역줄기, 미역귀, 다시마, 톳)중 톳을 제외하고는 모두 필름이 제조되었다. 이들 해조 필름의 물성에 대한 CaCl2 처리방법의 영향은 수분용해도 외에는 큰 차이를 나타내지 않았다. 비록 이들 해조필름의 인장강도, 투습도, 수분용해도와 같은 필름의 물성이 순수한 알긴산으로 제조한 필름의 물성에 비해 떨어지나 본 연구의 결과는 미이용 해조분말이나 해조가공 부산물로 얻어지는 해조분말을 이용하여 새로운 생분해성 포장소재로 사용할 수 있는 가능성이 있음을 나타냈다.