As a study on energy generation using light pressure, a basic experiment was conducted to compare the strength of the peak through SERS(surface-enhanced Raman sattering) measurement inside the crater after making a crater-shaped structure on a GaAs wafer and depositing an Au thin film. Then, an LPEG(light pressure electric generator) device by using 50nm nanoparticles was fabricated, and the completed device was evaluated by measuring the I-V(current-voltage) value in the environment of the solar simulator. This is the result of the pressure generated when the electromagnetic wave amplified through the plasmon passes through the crevice space inside the crater, and the magnitude can be evaluated by the electrical energy generated through the piezo material inside the device, and the measured energy density was obtained as Max. 576.8㎼/cm2. It was confirmed that the LPEG device manufactured through the experiment outputs stable DC power in a solid environment, and the application possibility was confirmed by driving the LED(Light-Emitting Diode) with the energy generated through this.

한국어

광압을 이용한 에너지 생성에 관한 연구로서 GaAs wafer에 crater 형태의 구조를 만들고 Au 박막을 증 착한 후, Au 나노입자를 부착하고 crater 내부의 SERS(surface-enhanced Raman scattering) 측정을 통하여 peak의 강도를 비교하는 기초실험을 진행하였다. 그리고 50nm 크기의 나노입자를 이용해서 LPEG(light pressure electric generator) 디바이스를 제작하였고 완성된 디바이스는 solar 시뮬레이터의 환경에서 I-V(전류-전압) 값을 측정하여 특성을 평가 하였다. 이는 crater 내부에서 플라즈몬을 통해 증폭된 전자기파동이 crevice 공간을 통과하 면서 발생된 압력의 결과로 나타난 것으로서, 그 크기는 디바이스 내부의 피에조 물질을 통해서 발생된 전기에너 지로 평가할 수 있는데, 측정한 에너지 밀도는 Max. 576.8㎼/cm2 값을 얻었다. 실험을 통해서 제작한 LPEG 디바 이스는 solar 환경에서 안정적인 DC 전원이 출력되는 것을 확인하였으며, 이를 통해서 생성된 에너지로 LED (light-emitting diode)를 구동시켜 응용 가능성을 확인 하였다.