Optical and Mechanical Properties of Commercial Dental Enamel Porcelain
초록
영어
In this study, optical and mechanical properties were investigated with 4 kinds of commercialdental enamels. As a result of EDS analysis SiO2, Na2O, Al2O3and K2O were the main components of commercialdental enamels. In case of H specimen, content of SiO2and K2O were more than that of anotherspecimens. Starting powder and fired specimens were glass ceramics which were consist ofamorphous phase and leucite (crystalline) phase. Crystallization did not occurred during firingprocess, since the XRD peak intensity was similar between starting powder and fired specimens.As a result of differential thermal analysis, Tgand crystalline temperature was varied withcomposition in the range of 548~576and 735~780respectively. 0.5thickness dental enamelspecimens showed sufficient translucent properties. However, transmittance and reflectance werelower than 5% result from scattering due to the refractive index difference between glass andcrystalline phase. 3 point bending strength was in the range of 73.9~101.8MPa which was similaror slightly higher than enamel of natural teeth and Vickers hardness was higher than enamel ofnatural teeth more than 100.
목차
Ⅰ. 서론
Ⅱ. 연구방법 및 재료
1. 시편준비
2. 측정 및 방법
Ⅲ. 연구결과 및 고찰
1. 치과용 법랑질도재의 조성 및 상분석
2. 치과용 법랑질도재의 열적 특성 분석
3. 치과용 법랑질도재의 광학적 특성 분석
4. 치과용 법랑질도재의 기계적 특성 분석
5. 치과용법랑질도재의미세구조
Ⅳ. 결론
참고문헌