The purpose of this study was to compare the hardened lump components of gypsum powder used in skin care with the powder particles after kneading and applying it to the skin in the form of a pack. As part of the study to identify the microstructural characteristics of newly formed crystals in the hardened gypsum lump, the gypsum powder particles were first observed and analyzed using a scanning electron microscopy. Gypsum powder consists of fine particles and plate-shaped and cylindrical crystals. The fine particles were observed as feather-like in a low-magnification scanning electron microscope, and the size of a single particle varied from 100㎚ to 5㎛ in a high-magnification observation. The plate-shaped gypsum crystals measured 104㎛ in vertical length and 75㎛ in horizontal length. In addition, the edges of the plate-shaped crystals were rough and irregular. The columnar crystals were 208㎛ long and had a very smooth surface. In conclusion, the shape of gypsum powder consists of particulate, plate-shaped, and cylindrical crystals, but further research is required on the bonding state between crystals in solidified gypsum.

한국어

본 연구는 피부관리에 사용하는 석고 파우더를 반죽하여 팩의 형태로 피부에 바른 후 경화된 결정체를 파우더 입자와 비교 분석하기 위한 목적이 있다. 석고 팩에 새롭게 형성된 결정체의 미세구조적 특성을 석고 파우 더 입자와 비교 분석하기 위한 연구의 하나로, 우선 석고 파우더 입자를 주사전자현미경으로 관찰하여 분석하였다. 석고 파우더는 미세입자상 물질과 판상 및 원주형 결정체로 구성되어 있다. 미세 입자상 물질은 저배율의 주사전자 현미경 상에서 깃털 모양으로 관찰되었고 고배율 관찰에서 단일 입자 결정의 크기는 100㎚에서부터 5㎛까지 다양 하였다. 판상의 결정체는 장축 길이가 104㎛로 측정되었고 단축 길이는 75㎛로 측정되었다. 그리고 판상의 결정체 가장자리는 거칠고 불규칙하였다. 기둥 모양의 원주형 결정체는 길이가 208㎛로 나타났으며, 표면이 아주 매끄러 웠다. 결론적으로 석고 파우더의 모양은 입자상, 판상, 원주상 결정체로 구성되어 있지만, 향후 응고된 석고에서 이들 결정체의 형태적 변화와 결정체 사이의 결합 상태에 관한 추가 연구가 요구된다.