This study compared the corrosion thickness of iron artifacts using both non-destructive and destructive analytical methods. More specifically, the study evaluated the effectiveness of non-destructive neutron diffraction in measuring corrosion. Neutron diffraction analysis indicated a measurement error of approximately 6% when compared to the results of the other methods, confirming its applicability in assessing corrosion thickness in iron artifacts. The results were in line with those of previous studies. In addition, a results comparison with destructive analysis confirmed that the corrosion thickness of DPL(Dense Product Layer) could be estimated using the non-destructive neutron diffraction method when considering the characteristics of TM(Transformed Medium). This method of estimating the corrosion thickness and internal structures of iron artifacts through neutron analysis and without causing damage significantly enhances our understanding of iron corrosion while verifying its potential for use in practical applications.

한국어

본 연구는 철제유물의 부식두께에 대해 비파괴 및 파괴분석 결과와 비교하여, 비파괴적 인 중성자 회절법을 이용한 철제유물의 부식 측정의 적용 가능성을 확인하였다. 중성자 회절을 이용한 부식두께는 각 분석법을 적용한 결과와 비교했을 때 오차범위가 약 6%이며, 이는 선행 연구 결과와 비교하였을 때 철제유물의 부식두께를 측정함에 있어 적용성이 큼을 확인하였다. 또한, 파괴분석 결과와 비교하였을 때, TM의 특성을 고려하면 비파괴적인 중성자 회절법을 이용하여 DPL의 두께를 추정할 수 있음을 확인하였다. 이렇듯 중성자를 이용하여 파괴하지 않고 철제유물의 부식두께 및 내부구조를 추정하는 방법은 철제유물의 부식을 이해하는 데 있어 큰 도움을 줄 수 있으므로 그 활용 가능성이 큼을 확인하였다.