Wood plastic composite(WPC) are widely used in various industrial fields due to their lightweight and excellent mechanical properties. In this study, WPC was manufactured by recycling waste Korean pine that were discarded as a forest by-product. The aim was to reduce social costs and improve the performance of WPC with environmental benefits and antibacterial properties. For this purpose, WPC was manufactured using PVC, wood fiber and Korean pine fiber. The strength characteristics, specific gravity and antibacterial properties of the WPC were examined. The maximum flexural load of the WPC using Korean pine fiber ranged from 2,640 to 4,860N, compared to 4,350N in the control sanple. The impact strength showed excellent characteristic in the range of 7.4 to 16.2kJ/m² and the specific gravity was 0.95 to 1.00 showing lightweight characteristics. The WPC manufactured with Korean pine fiber showed excellent properties and antibacterial effects, suggesting a strong potential for industrial applications.

한국어

합성목재(Wood Plastic Composite, WPC)는 경량성과 우수한 기계적 특성으로 인해 다양한 산업 분야에서 널리 활용되고 있다. 본 연구에서는 산림 부산물로 폐기되었던 폐잣송이를 재활용하여 WPC를 제조함으로써, 사회적 비용 절감과 환경적 이점, 그리고 항균성을 갖춘 합성목재의 물성 향상을 목표로 하였다. 이를 위해 PVC, 목재 섬유 (wood fiber), 및 잣송이 섬유(Korean pine fiber)를 사용하여 WPC를 제조하였다. 제조된 WPC의 강도 특성, 비중 및 항균성을 평가하였다. 최대 굴곡 하중은 대조군의 4,350N에 비해 잣송이 섬유를 사용한 WPC에서 2,640 ~ 4,860N의 범위를 나타내었다. 충격 강도는 7.4 ~ 16.2kJ/m²로 우수한 특성을 보였으며, 비중은 0.95 ~ 1.00으로 경량 성을 유지하였다. 결론적으로, 잣송이 섬유를 활용한 WPC는 뛰어난 물리적 특성 및 항균성을 나타내어 잠재적인 산 업적 적용 가능성이 높음을 확인하였다.