　In this study, carbon nanotubes (CNTs) were coated on three different flexible and stretchable rubber materials, and optical, electrical, and mechanical properties were analyzed. A novel method of coating a solution-based CNT material on the rubber surface using a finger-worn rubber was performed. And then a CNT-based thin film was formed through subsequent heat treatment. Samples were produced by repeating the coating process two times on each rubber. The surface roughness of the rubbers decreased through the CNT coating. The light-responsive characteristics (reflectivity, transmittance, and absorbance) of the three different rubbers were measured and analyzed. The phenomenon of reflectance, transmittance, and absorbance alternately increasing and decreasing above 1,100 nm was observed in all samples. It was confirmed that there was no difference in surface resistance before and after repeated bending of a CNT thin film formed on a rubber substrate up to a bending radius of curvature of 0.2 mm for 200,000 cycles. However, in the evaluation of stretchable properties, when stretched to approximately 1.5 times its original length, the CNT network was disrupted, and resistance could no longer be measured. This remains a challenge to be addressed in the future.

한국어

본 연구에서는 플렉서블 및 스트레처블 가능한 3가지 서로 다른 고무소재들 상에 탄소나노튜브(CNT)를 코팅하여 광 학 및 전기적, 기계적인 특성을 분석하였다. 고무상에 용액 기반의 CNT 물질을 손가락에 낀 고무를 이용한 신개념의 방법으 로 용액을 전면에 코팅하고, 후속 열처리를 통해 CNT 기반의 박막을 형성하였으며, 이와 같은 방법으로 각 고무상에 총 2번 의 코팅 공정을 반복하여 샘플들을 제작하였다. CNT 코팅을 통해 고무들의 거칠기가 감소하는 경향을 확인하였다. 3가지 서 로 다른 고무에 대해 빛과의 반응 특성(반사도와 투과도, 흡수도)를 측정 및 분석하였으며, 반사도, 투과도, 흡수도 모두 1,100nm 이상에서 증가와 감소를 반복하는 현상이 모든 샘플에서 관찰되었다. 고무상에 형성된 CNT 박막의 벤딩에 따른 전기적인 특성 변화를 곡률반경 0.2mm까지 반복적으로 200,000번 벤딩 진행 전후 표면 저항 값에 차이가 없음을 확인하였 다. 하지만, 스트레처블 특성 평가에서는 원래 길이의 약 1.5배 이상으로 늘어났을 때 CNT의 연결고리들이 끊어져 저항값이 측정되지 않았으며, 향후 해결해야 할 과제가 될 것이다.