This study examined the material characteristics and firing temperatures according to the type and period of the potteries and roof tiles excavated from Gongsanseong Fortress, the royal palace of Woongjin Baekje, through the scientific analysis. The potteries are characterized by the bowl, long-oval, tripods and lid shaped, respectively, and there are differences in the Woongjin and Sabi periods. In chemical compositions of the body clay, the potteries and roof tiles have similar compositional variations, but there are slight differences in the enrichment and deficiency of some elements depending on the period. Especially, Fe2O3 contents are some different in the bowl and long-oval shaped potteries, and CaO is slightly enriched. Contents of Al2O3 shows also slightly different depending on the type and period. This seems to be influenced by the refinement degree of the body clay, and it was confirmed that the tripods and lid shaped potteries were relatively homogeneous, and fired at relatively high temperature. Based on the mineral phase changes and thermal analysis, their firing temperatures are interpreted as follows as the potteries of the Woongjin and Sabi periods are classified into 850 to 900℃ and 1,000 to 1,050℃ depending on the type, and Woongjin and Sabi roof tiles are indicated at around 950℃ and 1,050℃, respectively.

한국어

이 연구에서는 웅진백제의 왕성이었던 공산성 출토 일부 토기와 기와의 과학적 분석을 통해 기종과 시기에 따른 재질특성과 소성온도를 검토하였다. 연구대상 토기는 발형과 장란형 및 삼족기 와 뚜껑으로 각각 웅진기와 사비기의 특징이 있으며, 기와에서도 시기에 따른 차이가 나타난다. 태토 의 화학조성으로 볼 때 토기와 기와는 유사한 조성변화를 가지나, 시기에 따라 일부 원소에서 부화와 결핍의 미세한 차이가 있다. 특히 Fe2O3는 발형과 장란형 토기에서 다소 편차가 있으며 CaO가 약간 부화되어 있고, Al2O3도 기종과 시기에 따라 조금 다르다. 이는 태토의 정선도에 영향을 받은 것으로 보이며, 삼족기와 뚜껑에서 상대적으로 균질하고 비교적 고온에서 소성된 것으로 확인되었다. 결정 상 변화 및 열분석을 근거로 이들의 소성온도를 해석하면, 웅진기와 사비기 토기는 기종에 따라 850∼900℃ 및 1,000∼1,050℃로 구분되며, 웅진기와 사비기 기와는 각각 950℃ 및 1,050℃ 내외를 지시하였다.