As a result of scientific analysis of 26 pottery excavated from the DongOe-dong site in Goseong, pottery with various firing degrees was confirmed, ranging from low-firing pottery with mica minerals detected to high-firing pottery with high-temperature minerals such as cristobalite and mullite detected. In addition, low-firing pottery has an absorption rate of 9.7∼25.8% and generally shows high saturation value. On the other hand, high-firing pottery has low absorption rate and saturation value, so the physical characteristics of the pottery show a high correlation with the group classified by XRD analysis. Pottery with a low firing degree commonly contains fine-grained mineral particles and has a similar composition of trace elements such as Rb, Ba, and Sr. And they were most abundantly excavated from the No. 1-1 moat. However it was confirmed that there is a difference in the production area because compositions of the rare earth elements are distributed in two areas in the graph. High&intermediate-firing pottery samples are observed to have a vitrified base matrix and relatively less temper minerals. And their contents of Rb, Sr, and Ba are significantly different from low-firing pottery. In the composition of rare earth elements, they are all distributed in same area as one of the separated areas of low-firing pottery, so it is highly likely these pottery were produced in the same or nearby production region regardless of the firing degree. As a result of checking up the composition of rare earth elements according to the archaeological chronology of pottery, it is estimated that there was a change in the production region of the pottery introduced into the DongOe-dong site around 250 AD.

한국어

고성 동외동유적에서 출토된 토기 26점에 대한 과학적 분석을 실시한 결과 토기는 운모 류 광물이 검출된 연질토기부터 Cristobalite, Mullite 등의 고온 생성 광물이 검출되는 도질토기 까지 다양한 소성도를 갖는 토기가 확인되었다. 또한 낮은 소성도의 토기는 9.7∼25.8%의 흡수 율이며 내⋅외면, 속심의 채도가 대체로 높은 특성을 보인다. 반면 높은 소성도 토기는 흡수율, 색도 등이 모두 낮게 측정되어 토기의 물리적 특성은 XRD 분석에서 분류한 그룹과 높은 상관 성을 보인다. 소성도가 낮은 토기는 1-1호 환호에서 가장 많이 출토되었으며, 대체로 태토 내에 세립질∼중립질 입자가 포함되어 있고 Rb, Ba, Sr 등의 미량원소 조성이 유사하다. 그러나 희토 류원소 조성에서 두 영역으로 분리되어 분포하여 생산지에 차이가 있음이 확인되었다. 상대적 으로 높은 소성도의 토기는 유리질화된 바탕기질과 적은 비짐 광물이 관찰되고 미량원소 함량 이 연질토기와 큰 차이를 보인다. 희토류원소 조성에서는 분리된 연질토기 조성과 같은 영역에 모두 분포하고 있어 이러한 토기는 소성도와 관계없이 생산지가 같거나 인근한 지역에서 제작 되었을 가능성이 높다. 토기의 고고학적 편년안에 따라 희토류원소 조성을 검토한 결과 AD 250년을 전후한 시기에 동외동유적에 유입된 토기 생산지에 변화가 있었던 것으로 추정된다.