Purpose: In this study, PCM was used to give thermal performance to concrete and analyze its effect on durability to prevent disasters that may occur in concrete when exposed to hot and cold environments. Method: After preparing concrete specimens containing 10, 30, and 50% of the two types of PCMs compared to the cement volume, the pore volume, freeze melting resistance, and scaling resistance were evaluated. Result: Regardless of the type, when PCM powder was mixed with concrete, the amount of pores decreased, and when 10% and 30% were mixed, the freeze-melting resistance was also improved. It was also confirmed that the higher the mixing amount, the better the scaling resistance. Conclusion: When mixing powdered PCM into concrete, it is believed that durability can be improved to a certain level by the filling effect, and additional various studies should be supported for actual field application.

한국어

연구목적: 본 연구에서는 혹서 및 혹한 환경에 노출 콘크리트에서 발생할 수 있는 재난을 방지하기위해 PCM을 활용해 콘크리트에 열성능을 부여하고 내구성에 미치는 영향을 분석하였다. 연구방법: 두 종류 의 PCM을 시멘트 부피대비 10, 30, 50% 혼입한 콘크리트를 제작한 후 공극량, 동결융해 저항성, 스케일 링 저항성을 평가하였다. 연구결과: 종류에 상관없이 PCM 분말을 콘크리트에 혼입할 경우 공극량이 감 소되는 것으로 나타났고 10%, 30% 혼입시 동결융해 저항성 또한 향상되는 것으로 나타났다. 또한 혼입 량이 높아질수록 스케일링 저항성이 향상되는 것을 확인하였다. 결론: 분말형태의 PCM을 콘크리트에 혼입 시 일정수준까지는 채움효과에 의해 내구성을 향상시킬 수 있을 것으로 판단되며 실제 현장 적용 을 위해서는 추가적으로 다양한 연구가 뒷받침 되어야 할 것으로 사료된다.