Fatty acids, tall-oil, reaction products with tetraethylenepentamine and 1-(2-aminoethyl) piperazine-based epoxy resin were mixed to manufacture 2 types of hardener to enable hardness control for restoration of earthenware. The mixed epoxy resin was manufactured in 2-solution reaction hardening type to control the hardness in the range of approximately 40∼65 Hs, and tensile strength in the range of 27∼121 kgf/mm2 and hardening type of 20∼30 min were secured. Moreover, it has wear rate that has been enhanced by 2 folds compared to the existing restoration material, which can be controlled in accordance with the mixing ratio, and was manufactured to enable mixing of diversified fillers later on. These results indicate that this is a restoration material that can solve the problems pointed out for the earthenware restoration materials such as processability and workability that occurred due to high level of hardness, tensile force and adhesion strength, etc., and increase in the level of fatigue due to tension with earthenware surface, etc. Accordingly, it is deemed that it is a material that can be used in actual restoration.

한국어

토기 복원을 위한 경도 조절이 가능하도록 Fatty acids, tall-oil, reaction products with tetraethylenepentamine와 1-(2-Aminoethyl)piperazine를 기반으로 한 에폭시 수지를 혼합하여 2 종 의 경화제를 제조하였다. 혼합된 에폭시 수지는 2액 반응 경화형으로 제조되어 약 40∼65 Hs 내외에서 경도를 조절할 수 있었으며, 27∼121 kgf/mm2의 인장강도와 20∼30 min의 경화시간 을 확보하였다. 또한 기존의 복원 재료보다 2 배 증진된 마모율과 이를 배합 비율에 따라 조정 할 수 있으며, 향후 다양한 충전제가 혼합 가능하도록 제조하였다. 이러한 결과는 토기 복원 재료의 문제점으로 지적되었던 강한 경도와 인장성, 접착력 등으로 인해 발생했던 가공성, 작업 성, 경화 후 토기 표면과의 장력으로 인한 피로도 증가 등을 해결할 수 있는 복원 재료를 제시하 고 실제 복원에 사용될 수 있는 재료로 판단된다.