The tribology characteristics of the graphene coated PA6 were evaluated with scratch experiments. As a result, the following conclusions were obtained. The PA6 of the graphene coating shows a 0.1 improvement in friction coefficient and a lower abrasion depth than PA6 in the variable pressure-type scratch experiments. PA6 of the graphene coating showed a lower friction coefficient of 0.2 or more than PA6 in the friction coefficient in the static pressure scratch experiments, indicating that wear resistance was improved. In both the variable and the static pressure type scratch experiments, the tip depth of graphene-coated PA6 shows a thinner wear depth than PA6, showing the effect of graphene. The graphene content showed excellent tribology characteristics at 3%, and there was no difference in tribology characteristics at higher contents.