The effect of La0.7Sr0.3MnO3 (LSMO) addition on the superconducting property of Bi1.6 Pb0.4Sr2Ca2Cu3O10+δ ((Bi, Pb)-2223) polycrystalline samples was studied. LSMO (0.3 wt.% to 2.0 wt.%) added (Bi, Pb)-2223 samples were prepared by using a solidstate reaction method. The XRD analyses show that as the LSMO addition increases, the volume fraction of the Bi-2223 phase is gradually decreased. The critical temperature (Tc) exhibits a gradual decrease with a single transition as the LSMO amount increases up to 1.0 wt.%, but a further addition of LSMO induces an abrupt decrease of Tc with a dual transition. The analyses on the local structure of the CuO2 plane from the X-ray absorption fine structure (EXAFS) measurements showed that for the samples with low concentration of LSMO up to 1.0 wt.%, the Cu-O bond length and the CuO2 plane ordering do not degrade from the values of pure (Bi, Pb)-2223, while they get worsen with a further increase of LSMO addition. These results open up the possibility of LSMO as artificial pinning centers of the (Bi, Pb)-2223 system for power application.
목차
1. INTRODUCTION
2. EXPERIMENTAL DETAIL
3. RESULT AND DISCUSSION
4. CONCLUSION
ACKNOWLEDGMENT
REFERENCES