Cementitious composites have excellent tensile performance and damage control performance, and when used as seismic reinforcement, they have many advantages as they exhibit strain hardening behavior in which stress increases with deformation without decreasing stress even after initial cracking. The mixing time, fiber dispersion, flow, segregation, unit weight and plastering were evaluated for cementitous composite with the optimal mix design. As a result of the evaluation, the sand mixing ratio of sand type-3 was 40%, the filler mixing ratio of filler type-3 was 15%, the polymer mixing ratio of polymer type-2 was 5%, the superplasticizer mixing ratio of superplasticizer type-3 was 0.2%, and the defoaming agent mixing ratio was 0.2%, When the conditions of the evaluation items were satisfied. It is believed that the developed cementitous composite can be applied to seismic reinforcement technology that allows partial reinforcement.

한국어

고인성복합체는 인 성능 및 손상제어 성능 등이 탁월하여 내진보강재로 활용할 경우 초기균열 이후에도 응력의 저하 없이 변형의 증대와 함께 응력이 증대되는 변형경화거동을 보이고 무해한 복수의 미세균열인 멀티플크랙 특성을 발현하는 등의 장점이 있다. 최적배합설계를 한 고인성복합체를 대상으로 하여 비빔시간, 섬유 분산성, 플로우, 재료분리 유무, 단위중량 및 미장성을 평가하였다. 평가한 결과, 모래 유형-3의 모래 혼입률 40%, 필러 유형-3의 필러 혼입률 15%, 폴리머 유형-2의 폴리머 혼입률 5%, 고성능감수제 유형-3의 고성능감수제 혼입률 0.2%, 소포제 혼입률 0.2%일 때 평가항목의 조건을 만족하여 개발한 고인성복합체는 부분 보강이 가능한 내진보강 기술에 적용이 가능할 것으로 판단된다.