This study manufactured cement by replacing the existing raw material, coal ash with pond ash, and the quality characteristics were analyzed. Thus, the possibility of using pond ash as a cement raw material was verified. The main chemical components of conventional coal ash and pod ash is similar, but there is a notable difference in content. Thus, it is necessary to fine-tune the raw material mixing ratio to addess the variance. As a result of deriving the mixing ratio of the raw materials, up to 3.0% pond ash can be used. The main chemical components of the clinker using existing coal ash and pond ash were similar. Thus, this indicates that the use of pond ash during the clinker calcination does not have a significant effect on the chemical composition. The calcined clinker was crushed to produce cement. Cement using existing coal ash and pond ash showed a difference in setting time of about 10 minutes and compressive strength of 0.5 MPa. Consequently, this verified that the cement quality using coal ash and pond ash was equivalent.

한국어

화력 발전소에서 발생하는 부산물인 석탄회는 시멘트 원료의 대체재로 사용되고 있다. 기술·경제적 요인 으로 재활용되지 못하여 매립되는 석탄회는 대부분 해안 매립으로 다량의 염화물을 포함하고 있다. 본 연구에서는 시멘트 제조 원료 중 기존 석탄회를 매립회로 대체하여 시멘트를 제조하고, 품질 특성을 분석하여 매립회의 시멘트 원료 활용 가능성을 검토하였다. 실험결과 기존 석탄회와 매립회의 주요 화학성분(SiO2, Al2O3, Fe2O3 및 CaO)은 유사하나, 약간의 함량 차이로 동일 모듈러스 확보를 위해 원료의 미세조정이 필요하였다. 배합비 도출 결과 매립 회는 3.0%까지 사용 가능한 것으로 나타났다. 기존 석탄회 및 매립회 사용 클링커의 주요 화학성분(SiO2, Al2O3, Fe2O3 및 CaO)은 거의 동일하게 나타나, 클링커 소성 시 매립회의 사용은 클링커 화학성분에 유의미한 영향을 미 치지 않는 것으로 판단된다. 소성된 클링커를 분쇄하여 최종적으로 시멘트를 제조하였으며, 기존 석탄회 및 매립 회를 사용하여 제조한 시멘트의 물리적 특성 평가결과 응결시간은 약 10분, 압축강도는 0.5 MPa 차이를 나타냈 다. 따라서 시멘트 품질은 동등한 수준으로 제조됨을 확인하였으며, 결과적으로 매립회는 기존 시멘트 원료인 석 탄회를 대체할 수 있을 것으로 판단된다.