This study reviewed the use of soil injection materials using circulating resources as injection materials for the steel pipe multi-stage construction method. The tests performed were homogel time and homogel compressive strength. The steel pipe multi-stage construction method is an auxiliary construction method for tunnels, and the expression of initial strength after construction is an important factor. The better the strength development in the initial stage, the more it can be used as an injection material suitable for the multi-stage steel pipe construction method. As a result of laboratory test, it was found that the homogel time of the injection material using circulating resources required more time than the mixing ratio using cement as the injection material. In addition, it was found that the initial strength curing time satisfying 2MPa was required for more than 24 hours. Therefore, it was confirmed that the injection material using recycled resources required a longer initial curing time than cement of the same mixing ratio.

한국어

본 연구는 순환자원을 대량 활용한 지반안정재를 터널공사 시 보조공법으로 이용하는 강관다단공법의 주입재 로 활용을 검토하기 위해 다양한 주입재 배합비에 따른 겔타임, 호모겔 강도를 비교하였다. 강관다단공법은 터널의 보조공법으로써 시공 후 초기강도의 발현이 중요한 요인으로, 초기에 강도발현이 우수할수록 강관다단공법에 적합한 주입재로 활용이 가능하다. 실내시험 결과, 순환자원을 활용하는 주입재의 호모겔타임은 시멘트를 주입재로 활용하는 배합비에 비해 많은 시간이 필요한 것으로 나타났으며, 2.0MPa를 만족하는 초기강도 양생시간은 24시간 이상이 필요 한 것으로 확인되었다. 따라서 순환자원 활용 주입재는 동일 배합비의 시멘트에 비해 긴 초기경화 시간이 필요한 것 으로 나타났다.