Effects of special heat treatment on changes in the hardness of a metal-ceramic alloy during the firing process
초록
영어
Purpose: This study aimed to evaluate the effects of a special heat treatment on Pd-Au-Ag metal-ceramic alloy after degassing treatment and on changes in the hardness of the alloy during the firing process. Methods: Specimen alloys were cast and subjected to degassing at 900℃ for 10 minutes. These specimens were then subjected to a special heat treatment at 600℃ for 15 minutes in a dental porcelain furnace. Further, the specimens were subjected to simulated firing in the porcelain furnace. The resulting specimens were then tested for hardness, and changes in the microstructure were observed. Results: There was a decrease in the hardness of the alloy during the simulated firing of the cast alloy due to the coarsening of the particles. Meanwhile, additional heat treatment after degassing was found to play a crucial role in preventing a decrease in hardness. This treatment effectively suppressed the coarsening of the precipitates during repeated firing at high temperatures. Conclusion: Specific heat treatment of the Pd-Au-Ag metal-ceramic alloy prevented a decrease in its hardness and extended the lifespan of the metal-ceramic prosthesis.
목차
INTRODUCTION
MATERIALS AND METHODS
1. 시편 제작
2. 열처리
3. 경도테스트
4. 미세구조 변화 관찰
5. 통계처리
RESULTS
1. 추가 열처리가 모의소성 중 합금의 경도 변화에 미치는영향
2. 추가 열처리 후 모의소성에 따른 미세구조의 변화
DISCUSSION
CONCLUSIONS
FUNDING
ACKNOWLEDGEMENTS
CONFLICT OF INTEREST
ORCID
REFERENCES