In this study, the GAC adsorption processes were opereated by continuous and batchwise methods. The batchwise operation was used to investigage the effect of types of organic matter, and the continuous GAC operation was used to prepare the spent-GAC for Fenton regeneration test. The effect of Fe2+ and H2O2 moles concentration was investigated for the GAC regeneration efficiency in the Fenton oxidation treatment. The specific surfaces area and pore volumes of GAC were compared among the virgin-GAC, spent GAC and Fenton treated GAC using BET analysis, in addition, morphological characteristic of the GAC’s samples were observed through FE-SEM and EDS analysis. The GAC adsorption capacity was different with types of organic matter and the adsorption efficiency was shown in the order of methylene blue > sewage > sucrose. When the spent-GAC was regenerated by Fenton oxidation, the regeneration efficiency of GAC increased in proportion to the H2O2 amount, however, molar concentraion of the Fe2+ showed optimum dosage value for regeneration efficiency of GAC not having a linear relationship.

한국어

본 연구는 GAC 흡착공정을 연속운전과 회분식 테스트로 나누어 진행했으며 회분식 테스트는 용존유기물 종류가 GAC 흡착능에 미치는 영향을 조사했고 연속운전은 펜톤재생에 사용할 파과 GAC의 제조를 위해서 운전하였다. 펜톤산화를 통 한 GAC 재생반응에서 Fe2+ 및 H2O2 주입몰수가 GAC 재생효율에 미치는 영향을 조사하였고 신규 GAC, 파과 GAC 그리 고 펜톤처리 GAC에 대해 GAC의 비표면적과 세공부피 변화를 BET를 통해 비교 분석하였고 동일조건에서 형태학적 미세 구조 특성을 FE-SEM과 EDS를 통해 관찰하였다. 기질 종류에 따른 GAC의 흡착효율은 메틸렌블루 > 실하수 > sucrose의 순으로 나타났고, GAC 흡착은 기질 의존성이 매우 크게 나타났다. 파과된 GAC를 펜톤산화하여 재생처리할 때, 과산화수 소의 경우 주입량에 비례하여 GAC의 재생효율도 증가하는 것으로 나타났으나 촉매 역할을 하는 Fe2+은 주입량에 비레하 지 않고 최적주입량이 존재함을 의미하였고 과도한 Fe2+의 주입은 오히려 GAC의 재생효율을 감소시키는 결과를 나타났다.