Nickel oxide (NiO) nanoparticles were successfully synthesized by a simple liquid phase process for producing ceramics powder using a precursor impregnated with a nickel(Ⅱ) nitrate hexahydrate aqueous solution in an industrial pulp. The microfibrile structure of the precursor impregnated with nickel nitrate hexahydrate aqueous solution was confirmed by scanning electron microscope (SEM), and the crystal structure and particle size of nickel oxide (NiO) particles produced as the heat treatment temperature of the precursor were analyzed by X-ray diffraction (XRD) and SEM. As a result, it was confirmed through XRD and SEM analysis that the temperature at which the organic material of the precursor is completely thermally decomposed was 495-500°C, and the size and crystallinity of the nickel oxide particles produced increased as the heat treatment temperature increased. The size of the nickel oxide particles obtained by heat treatment at 500-800°C for 1 hour was 50-200 nm. It was confirmed by XRD and SEM analysis that a NiO crystal phase was formed at a heat treatment temperature of 380°C, only a single NiO phase existed until 800°C.

한국어

질산니켈육수화물염(nickel(Ⅱ) nitrate hexahydrate) 수용액을 공업용 펄프에 함침시킨 전구체를 이용하여 세라믹스 분 말을 제조하는 간단한 액상 합성법으로 산화니켈(NiO) 나노입자를 성공적으로 합성하였다. 질산니켈육수화물염 수용액이 함침 된 전구체의 미세구조를 주사전자현미경(SEM)으로 확인하였고, 전구체의 열처리온도 증가에 따라 생성되는 산화니켈(NiO) 입 자의 결정구조 및 입자크기를 X선회절분석(XRD) 및 SEM으로 분석하였다. 그 결과 전구체의 유기물질이 완전하게 열분해 되 는 온도는 495-500°C이며, 열처리 온도의 증가에 따라 생성되는 산화니켈 입자의 크기 및 결정성이 증가하는 것을 XRD, SEM 분석을 통하여 확인하였다. 500-800℃에서 각각 1시간 동안 열처리하여 얻어진 산화니켈 입자의 크기는 50-200nm였다. 열처리 온도 380℃에서 NiO 결정상이 형성되고, 800℃까지는 NiO 단일상만 존재하며, 열처리 온도가 높아짐에 따라 생성되는 입자의 크기가 커지고 있음을 XRD 및 SEM 분석으로 확인하였다.