To completely bond two or more metals, there is a method of applying heat or using a nail. Most bronze containers use nails to bond and repair, which are called rivet techniques. Until now, the manufacturing technology of bronze ware has been conducted by many researchers, but research on rivets used in bronze ware is insufficient. In order to understand the manufacturing technology of bronze ware, research on not only the main body of the container but also each part must be conducted together. In the case of rivets, it is believed that they were made in consideration of the material, color, and economic feasibility suitable for the Bronze Age, and in this study, metallic analysis was conducted focusing on the four rivets excavated. As a result of metal microscope and SEM-EDS analysis, it is judged that the Cu-Sn-Pb ternary alloy and Cu-Ag binary alloy were manufactured using the general casting method. Compared to previous studies, rivets can be divided into (1) 100% pure copper (Cu) (2) Cu-Sn-Pb ternary alloys (Sn, Pb around 10%), and (3) Cu-Ag binary alloys, and this time the analyzed rivets correspond to types (2) and (3). If you study not only rivets but also containers in the future, it will be helpful to understand the manufacturing technology process of bronze containers.

한국어

두 개이상의 금속을 완전하게 접합하기 위해서는 열을 가하거나 못을 사용하는 방법이 있다. 대부분의 청동용기에는 못을 사용하여 접합(결합)⋅수리를 하는데 이를 리벳기법(Rivet) 이라고 한다. 지금까지 청동기의 제작기술은 많은 연구자들에 진행되었으나 청동기에 사용되 는 리벳과 같이 접합⋅수리와 관련된 연구는 부족한 실정이다. 청동기의 제작기술을 이해하기 위해서는 용기 등의 본체뿐만 아니라 각 부위에 대한 연구가 함께 이루어져야 한다. 리벳의 경우, 청동기에 맞는 소재, 색상, 경제성 등을 고려하여 제작되었을 것으로 보고 있으며 본 연구 에서는 출토된 리벳 4점을 중심으로 금속학적 분석을 진행하였다. 금속현미경 및 SEM-EDS 분석결과, Cu-Sn-Pb 삼원계 합금과 Cu-Ag 이원계 합금으로 일반적인 주조방식으로 제작된 것 으로 판단된다. 이전 연구와 비교했을 때, 리벳은 (1) 100%에 가까운 순동(Cu) (2) Cu-Sn-Pb 삼원계 합금(10% 내외의 Sn, Pb), (3) Cu-Ag 이원계 합금으로 나눌 수 있으며 이번에 분석한 리벳의 경우는 (2), (3) 유형에 해당됨을 알 수 있었다. 추후 리벳뿐만 아니라 용기 등을 함께 연구한다면 청동용기의 제작기술 과정을 이해하는 데 도움이 될 것으로 보인다.