A Study on Industrial Glove Characteristics for IT Devices with Durability and Functionality
초록
영어
In this study, composite yarns and industrial gloves were manufactured using nylon yarn, Oxy PAN/FR Rayon blended yarn and copper yarn to give durability and functionality to industrial gloves for IT devices. In addition, the physical properties, flame retardancy, antibacterial and electrostatic properties of the composite yarn and glove fabric were analyzed. The composite yarn containing the Oxy PAN/FR Rayon blended yarn with and without adding copper yarn in the nylon yarn increased in strength and decreased in elongation compared to the conventional one. Tensile strength of the glove fabric increased significantly as the fineness increased as the content of Oxy PAN/FR Rayon blended yarn and copper yarn increased. Due to the knit structure of the glove fabric, the tensile strength is higher in the Course direction than in the Wale direction. and the elongation showed a low value. The glove fabric containing Oxy PAN/FR Rayon blended yarn and copper yarn had excellent flame retardancy, and in particular, the copper yarn-containing fabric had excellent antibacterial and triboelectric functions.
한국어
본 연구에서는 IT 기기 산업용 장갑의 내구성 및 기능성을 부여하기 위해 나일론 원사, Oxy PAN/FR Rayon 혼방사 및 동사를 사용하여 복합사 및 산업용 장갑을 제조하였다. 그리고 제조된 복합사 및 장갑원단의 물 리적 특성과 난연성, 항균성 그리고 정전기 특성에 대해 분석하였다. 나일론 원사에 Oxy PAN/FR Rayon 혼방사 및 동사가 함유된 복합사의 강도가 증가하였고, 신도는 감소하였다. 장갑원단의 인장강력은 Oxy PAN/FR Rayon 혼방사 및 동사 함유로 섬도가 증가할수록 강력은 크게 증가하였다. 장갑원단의 니트 구조상 Course 방향이 Wale 방향보다 인장강력은 높고, 신도는 낮은 값을 보였다. Oxy PAN/FR Rayon 혼방사와 동사가 함유된 장갑 원단은 난연성이 우수하였고, 특히 동사 함유 원단에서는 항균성 및 마찰대전성의 기능성이 우수하였다.
목차
Abstract
Ⅰ. 서론
Ⅱ. 실험 방법
2.1 사용 원사
2.2 복합사 및 장갑원단 제조
2.3 실험 방법
Ⅲ. 결과 및 고찰
3.1 복합사 및 장갑원단의 물리적 특성
3.2 장갑원단의 기능성 분석
Ⅳ. 결론
REFERENCES