earticle

영어

Applying the calculated cross-sectional reduction due to the corroded rebar investigated in the field to the numerical analysis model, the damage pattern and delamination of concrete in the field showed a tendency relatively similar to the numerical analysis results. It was analyzed that when the expansion pressure due to corrosion of the reinforcing bar is greater than the tensile stress of the concrete, cracks are generated and the concrete cover can be fracture. As a result of this study, the correlation between the corrosion rate of reinforcing bars and the crack occurrence of the concrete cover of the subway box structure was verified based on the numerical analysis and field test results. To prevent rebar corrosion, the corrosion rate can be reduced by applying rust prevention to the reinforcing bar and changing the material. In the case of exposed to a corrosive environment, the tensile strength of the concrete is improved by adjusting the concrete compressive strength to secure durability against the expansion pressure caused by the corroded rebar.

한국어

도시철도 지하구조물에서 중요한 열화 중 하나인 철근부식은 철근의 부피 팽창에 의해 콘크리트의 피복층의 균열 또는 표면박리, 박락 등을 초래하여 철근콘크리트 구조물의 사용성과 안전성이 저하된다. 본 연구에서는 부식 환경에서의 도시철도 지하박스 구조물을 대상으로 철근부식으로 인한 콘크리트 피복층의 균열발생 위치에서 철근의 팽창율을 측정하고 이를 바탕으로 철근부식으로 인한 콘크리트 피복층 들뜸 및 손상에 대한 분석을 수행하였다. 부식 된 철근의 방사형 변위 분포 모델을 산출하고 기존 제안식과 비교, 분석하였다. 또한 대표 단면을 대상으로한 수치해 석(역해석)을 수행하여 부식철근의 방사형 변위장에 의한, 철근의 불균일한 부식팽창을 해석모델에 적용하였다. 수치 해석 결과를 바탕으로 철근부식율 진전에 따른 철근콘크리트 구조물의 균열 및 피복층 박리의 영향을 해석적으로 도 출하고 현장 시료와의 비교를 통해 수치모델의 적정성을 입증하였다.