Characteristics of Corrosion Layers and Corrosion Products by Lead Contents of Excavated Bronze Artifacts
초록
영어
This study aims to investigate the corrosion characteristics of bronze artifacts according to lead contents by conducting a comprehensive analysis on corrosion layers and corrosion products focusing on excavated bronze artifacts of ternary alloys with various chemical compositions. From the research outcome, the selective corrosion, high-tin corrosion layers, and lead compounds were identified in two excavated bronze artifacts, and there was a difference in the structure of corrosion layers and the corrosion products of core metal between high lead content bronze and the lowest lead content bronze. Especially, based on the specimen with the highest lead content, it was identified that lead oxide in reddish color and a large quantity of lead corrosion products including lead carbonate in various colors such as white, red, yellow, and green are distributed inside the base metal. In this study, the number of analyzed samples is insufficient to represent the corrosion characteristics of bronze artifacts made of the ternary alloys. Therefore, it is judged that basic data should be accumulated by conducting a corrosion characteristic study on bronze artifacts with various alloy composition ratios in the future.
한국어
본 연구에서는 다양한 화학조성의 삼원계 출토 청동유물을 대상으로 부식층 및 부식생성물 에 대한 종합적인 분석을 실시하여 납 함량에 따른 청동유물의 부식특성에 대해 연구하였다. 출토 청동유물 2점의 부식층 및 부식생성물 분석결과, 선택부식, 고주석부식층의 형성, 납화합물의 부식특성이 확인되었다. 또한 납 함량이 높은 시편과 납 함량이 낮은 시편은 부식층위구조와 소지금 속 내에 형성된 부식생성물의 종류 등에서 차이를 나타냄을 알 수 있었다. 특히 납 함량이 높은 시편에는 적색 계열의 산화납과 백색, 적색, 황색, 녹색 등의 다양한 색상을 가진 탄산납 계열의 부식생성물이 형성된 것을 확인하였다. 다만, 본 연구에서 분석한 사례만으로는 시료의 개수가 부족 하여 납 함량비에 따른 부식 경향성을 파악하기 어려우므로, 향후 다양한 합금조성비의 청동유물을 대상으로 한 부식층위구조 및 부식생성물 분석 연구가 진행되어야 할 것이다.
목차
ABSTRACT
1. 서론
2. 연구대상 및 방법
2.1. 연구대상
2.2. 연구방법
3. 연구결과
3.1. 부식층 층위구조 관찰
3.2. 부식생성물 관찰 및 성분분석
3.3. 부식생성물 화합물 분석
4. 고찰
4.1. 출토 청동유물의 부식특성
4.2. 출토 청동유물의 납 함량에 따른 부식특성
5. 결론
REFERENCES