This study investigated the characteristics for the optimal concentration of addition of the mixing solution through the corn husk pulverization and surface modification of biomass byproducts adding mixed solution between ESO and silane. And surveyed the specific surface area, water absorption, particle size and physical properties of bio- degradable plastic sheet. The specific surface area was 1.105m2/g, particle size was the highest at 19 μm. The impact strength, tensile strength, elongation and hardness of plastic sheet showed the highest at the 1% concentration among the mixing solutions. The flexural strength and modulus was high according to the increasing the mixing solution. The results above showed that it was the best the adding 1% of mixed solution after silane treatment of corn husks for its manufacture as a bio-based plastic sheet.

한국어

본 연구에서는 식량자산인 바이오매스 옥수수의 부산물 인 옥수수 피를 LLDPE에 첨가하여 바이오베이스 시트를 제조할 때 물성개선을 위한 상용화 혼합물의 적정 첨가량 을 찾고자 한다. 옥수수 피의 상용성을 높이고자 ESO와 실란 혼합물 실란을 농도별로 첨가하여 비표면적, 함수율, 입도분석 및 제조한 바이오베이스 플라스틱 시트의 물성변 화를 조사하였다. 비표면적은 1.105 m2/g, 입도는 19 μm에 서 가장 우수하였다. 시트의 충격강도, 인장강도, 신율 및 경도는 대조구에 비해 SI-1-CR은 높게 나타났으나 SI-2- CR과 SI-3-CR은 낮게 나타났다. 또 실란 혼합물 1% 처리 구에서 가장 높게 나타났다. 굴곡강도와 탄성율은 첨가량이 증가할수록 높게 나타났다. 생산 성도 대조구에 비해 큰 차 이가 없었으며, 원가의 경우도 바이오매스 부산물로 대조 구 석유계 합성 플라스틱 수지보다 50%이상 저렴하여 경 제성이 있다고 사료되었다. 이제품은 수퍼, 마트 등의 1회 용 봉투, 종량제 봉투 등에 사용될 수 있을 것이다. 이상의 결과로부터 실란 혼합물 1%를 첨가하여 바이오베이스 플라 스틱 시트를 제조하는 것이 바람직할 것으로 사료되었다.