This study investigated the characteristics for rice husk pulverization and surface modification of biomass byproducts composed of rice husk, corn extract gourd, wheat bran, and soybean curd. The size of particles of rice husk was at 6.44 μm and represented the most affordable material for preparing the bio-degradable film among the tested byproducts. The silane treatment and adding 2% of ESO (Epoxidized soybean oil) and 3-aminopropyl triethoxysilane solution mixed in a 1:1 ratio were best to the surface modification and SEM-based particle shape. Above the results, adding 2% of mixed solution after silane treatment of rice husks processed through an air classifying mill (ACM) allows for its use as a raw material of bio-degradable plastic film.

한국어

본 연구에서는 바이오매스 부산물을 바이오 플라스틱에 첨가할 수 있는지 여부를 찾고자 바이오매스 부산물인 왕 겨, 옥 피, 밀박, 대두박에 대해 일반성분을 조사하였다. 그리 고 왕겨에 대해 분체화, 표면 개질 특성을 조사하였다. 부산 물 중에서는 왕겨의 입도가 6.44 μm로 가장 적합하였으며, silane 처리 후 ESO(Epoxidiz soybean oil)와 3-aminopropyl triethoxysilane를 1:1로 혼합한 용액을 2% 첨가 시 표면개 질 상태가 가장 우수하였고, SEM에 의한 입자형상도 가장 좋은 것으로 나타났다. 따라서 ACM(air classifying mill) 처리한 왕겨를 silane 처리한 후 혼합용액을 2% 첨가하는 것이 표면이 개질된 바이오플라스틱 원료로 첨가하여 사용 할 수 있을 것으로 사료되었다.