메탄올 증기개질을 위한 Cu/γ-alumina 기반 촉매의 촉진제 사용에 따른 특성 연구
초록
영어
To prevent global warming due to the use of fossil fuels, many studies have been conducted on hydrogen production through methanol steam reforming. nevertheless, the effect of steam reforming by the promoters of the catalyst prepared by the use of the support and the impregnation method requires further study. therefore, through this study, basic physical properties such as catalyst surface properties and crystal state were observed according to the impregnation ratio of the promoters based on the Cu/γ-alumina support. in addition, by implementing methanol steam reforming, the effect of the composition of Zn and Zr used as promoters on the composition of steam reforming products was investigated. the basic physical properties of the catalyst could be observed through SEM-EDS, TPR, XRD. The hydrogen composition effect by zinc, which was expected to increase the hydrogen composition, was not clearly shown. however the effect on the carbon dioxide selectivity was well shown for both zirconium and zinc, and the Cu/Zn ratio of 1 showed better carbon dioxide selectivity by zirconium than the case of 2.5.
한국어
화석연료 사용으로 인한 지구온난화 방지를 위해 메탄올 증기개질을 통한 수소 생산 연구가 많이 진행되었으나, 지지 체 사용 및 함침법으로 제조된 촉매에서의 촉진제에 의한 증기개질 영향은 더 많은 연구가 필요하다. 따라서 본 연구를 통해 Cu/γ-alumina 지지체를 기반으로 촉진제 함침 비율에 따른 촉매 표면특성과 결정상태 등의 기초적인 물성을 확인하 고 메탄올 증기개질을 시행함으로서 촉진제로 사용된 Zn, Zr의 조성에 따른 증기개질 생성물 조성에 미치는 영향을 파악 하고자 하였다. 촉매의 기초 물성은 SEM-EDS, TPR, XRD를 통해 확인할 수 있었다. 수소 조성을 증가시킬 것으로 예상 되었던 Z n에 의한 수소 조성 영향은 본 실험에서 명확하게 나타나지 않았으나 이산화탄소 선택도에 대한 영향은 Z r과 Zn 모두 그 특성이 잘 나타났으며, Cu/Zn 비율이 1인 경우가 2.5인 경우에 비해 Zr에 의한 이산화탄소 선택도 면에서 더 좋게 나타났다.
목차
요약문
I. 서론
II. 연구방법
1. 촉매 제조 방법
2. 실험장치 및 방법
III. 결과 및 고찰
1. 촉진제 사용에 따른 SEM-EDS, XRD 결과분석
2. 촉진제 사용에 따른 TPR 분석
3. 촉진제 사용에 따른 증기개질 결과
IV. 결론
사사
References