In this study, a mixed resin containing Bis-GMA was developed to produce a light-emitting sign using quantum dots. As a result of measuring the viscosity, color coordinates change, and luminance of the mixed resin, the following conclusions were obtained. The viscosity of the mixed resin decreased as the content of the diluent increased, and viscosity values ranged from 3,627 to 1,349cps showed as a result. The viscosity of the mixed resin decreased as the temperature increased, and the viscosity showed a value of 5,156 to 1,132cps. For the optical properties of InP/GaP/ZnSe/ZnS quantum dots, the absolute quantum efficiency was 91% at 522nm and 90% at 618nm when the gallium was 0.01%. The luminance of the light-emitting sign using the resin mixed with quantum dots was showed 142.6cd/m2 in white and 104.2cd/m2 in the red region.
목차
1. 서론
2. 실험 및 방법
2.1 혼합 레진 제조
2.2 혼합 레진의 점도 측정
2.3 양자점 합성
2.4 양자점이 첨가된 광중합형 레진 제조
2.5 광학 특성 측정
3. 실험 결과
3.1 혼합 레진의 점도 측정 결과
3.2 온도 증가에 따른 점도 측정 결과
3.3 양자점의 광학 특성
3.4 발광 표지의 광학 특성
4. 결론
후기
References