Radiation shields used in medical institutions mainly use lead to manufacture products and fitments. Although lead has excellent processability and economic efficiency, its use is being reduced due to environmental issues when it is disposed of. In addition, when used for a long time, there is a limit to using it as a shielding film, shielding wall, medical device parts, etc. due to cracking and sagging due to gravity. To solve this problem, copper, tin, etc. are used, but tungsten is mostly used because there is a difficulty in the manufacturing process to control the shielding performance. However, it is difficult to compare with other shielding materials because the characteristics according to the type of tungsten are not well presented. Therefore, in this study, a medical radiation shielding sheet was manufactured in the same process using pure tungsten, tungsten carbide, and tungsten oxide, and the particle composition and shielding performance of the sheet cross-section were compared.As a result of comparison, it was found that the shielding performance was excellent in the order of pure tungsten, tungsten carbide, and tungsten oxide.

한국어

본 의료기관에서 사용되는 방사선 차폐체는 주로 납을 활용하여 제품과 부속품을 제작한다. 납은 가공성과 경제성이 우수하지만 폐기 시 환경 문제로 인해 사용량을 줄이고 있으며, 오랫동안 사용했을 시 크랙 현상과 중력 에 의한 처짐 현상으로 인해 차폐막, 차폐벽, 의료기기 부픔 등으로 장기간 사용하기에는 한계가 있다. 이러한 문 제점을 해결하기 위해 구리, 주석 등을 사용하지만, 아직 차폐성능을 제어하기에는 제작 공정에 어려움이 있어 대부분 텅스텐을 많이 사용하고 있다. 그러나 아직 텅스텐의 종류에 따른 특성이 잘 제시되지 못해 다른 차폐재와 의 비교가 어렵다. 따라서 본 연구에서는 순수 텅스텐, 탄화텅스텐, 산화 텅스텐을 이용하여 동일한 공정으로 의료 방사선 차폐시트를 제작하여 시트 단면의 입자 구성과 차폐성능을 비교하였다. 비교 결과 순수 텅스텐, 탄화텅스 텐, 산화 텅스텐 순으로 차폐성능이 우수한 것으로 나타났다.