Purpose: This study aimed to compare the flexural properties and perform the Weibull analysis of photo-curing three-dimensional (3D) printing resin. Methods: Photo-curing temporary resin (3D polymer) was used as a printing resin. Specimens (65 × 10 × 3.3 mm3) were prepared following the ISO 20975-1 guidelines and according to the different printing orientations using a digital light processing 3D printer (D2 120; Dentium). The flexural strength (FS), flexural modulus, and work of fracture (WOF) were measured using a universal testing machine (Instron 3344; Instron) at a crosshead speed of 5 mm/min. Results: In this study, the 0° orientation exhibited higher FS and WOF than the 45° orientation. Significant differences were found among the printing orientations (p<0.05). Specimens printed at the 0° orientation were the most accurate. In the Weibull analysis, 0° showed the greatest Weibull modulus (m), which represents a higher reliability. Conclusion: 3D printing should be selected and used by considering flexural properties, size accuracy, and reliability.