earticle

영어

This study was to investigate the effect of the new surface treatment method of zirconia on the shear bond strength with resin cement. The zirconia specimens were classified according to the surface treatment. CON: non-treatment, HF: 10 minutes exposure to 9% HF, ZS15: Apply 15% ZrO2 slurry, ZS30: Apply 30% ZrO2 slurry, ZS50: Apply 50% ZrO2 slurry. The resin cement was layered on the surface treated zirconia, and the shear bond strength between the zirconia and the resin cement was measured after thermo-cycling. The statistical methods for shear bond strength were Kruskal-Wallis test, Mann-Whitney U test, and Bonferroni correction(α=.05/10=.005). ZS15, ZS30, and ZS50 groups treated with zirconia slurry showed higher shear bond strength than CON and HF groups(p <.05/10=.005). Within the limits of this study, the surface treatment using zirconia slurry increased the shear bond strength with resin cement. The new surface treatment method complements and improves the limitations of the adhesion of zirconia, so that various clinical applications of zirconia can be expected.

한국어

본 연구에서는 지르코니아의 새로운 표면처리 방법이 레진 시멘트와의 전단결합강도에 미치는 영향을 알아보고 자 하였다. 지르코니아 표면처리 방법 따라 5개의 그룹으로 분류하였다: 표면처리 미시행한 군(CON군), 100℃에서 9% 불산에 10분간 노출시킨 군(HF군), 15% 지르코니아 슬러리를 적용한 군(ZS15군), 30% 지르코니아 슬러리를 적용한 군(ZS30군), 50% 지르코니아 슬러리를 적용한 군(ZS50군). 표면처리한 지르코니아 위에 레진 시멘트를 적용하였고, 열 순환 처리 후 지르코니아와 레진 시멘트 간의 전단결합강도를 측정하였다. 전단결합강도에 대한 통계 방법으로 Kruskal-Wallis test와 Mann-Whitney U test 및 Boneferroni correction를 사용하였다(α=.05/10=.005). 지르코 니아 슬러리를 적용한 군은 CON군과 HF군에 비해 높은 전단결합강도를 보였다(p <.05/10=.005). 지르코니아 슬러리 를 이용한 표면처리 방법은 레진 시멘트와 지르코니아 간의 전단결합강도를 증대시킴을 확인하였다. 본 연구 결과, 새로 운 표면처리 방법은 지르코니아가 지닌 접착의 한계점을 보완하고 개선함으로써 지르코니아의 보다 다양한 임상적 적용 가능성을 기대할 수 있을 것으로 사료된다.