There is an increasing interest in manufacturing various electronic devices on a bendable substrate. In this paper, we observed a surface morphology by annealing for 20 minutes at temperatures of 150 oC, 350 oC, and 550 oC, respectively, with samples coated by chromium and aluminum. Data on surfaces are investigated using high-resolution SEM and AFM that can measure roughness up to nm. There is no difference from the sample without heat treatment up to 350 oC, but the change of crystal grains can be observed at 550 oC. In the future, for application to the flexible optoelectronic field, additional characteristics such as electrical conductivity and reflectivity will be analyzed and optical devices will be manufactured. In conclusion, we will explore the possibility of applying metal materials to flexible electronic devices.

한국어

최근 폴리이미드가 기판으로 사용되어 유기발광다이오드 디스플레이가 구현된 폴더블 스마트폰이 출시되고 있다. 이와 같이 굽힘이 가능한 기판위에 다양한 전자소자를 제작하기 위한 관심이 증가하고 있기 때문에 본 논문에서는 굽힘성 이 우수한 127μm 두께의 얇은 스테인리스 금속 기판을 이용하여 먼저 크롬을 코팅하고 알루미늄을 형성한 샘플과 알루 미늄 구현 후 크롬을 증착한 2가지 샘플을 급속 열처리 장비를 이용하여 150도, 350도, 550도의 온도에서 각각 20분간 어닐링을 진행하여 표면의 형상을 관찰하였다. 고분해능 SEM과 nm까지 거칠기를 측정할 수 있는 AFM을 이용하여 표면 에 대한 데이터를 추출하였다. 350도까지는 열처리하지 않은 샘플과 차이가 없지만, 550도에서는 결정립의 변화를 확인 할 수 있다. 향후 본 실험 결과는 플렉서블 광전자분야로의 적용을 위해 전기전도도, 반사도와 같은 특성 분석 및 광소자 제작을 통해 금속 소재의 플렉서블 전자소자로의 적용 가능성을 모색할 것이다.