Comparison between mechanical properties and biocompatibility of experimental 3D printing denture resins according to photoinitiators
초록
영어
Purpose: In this study, we added two kinds of photoinitiators (CQ and TPO) to prepare two kinds of denture base resins (Bis-GMA series and UDMA series) for three-dimensional (3D) printing to compare and analyze their mechanical and biological properties and to find the optimal composition. Methods: Control specimens were made using the mold made of polyvinyl siloxane of the same size. Light curing was performed twice for 20 seconds on both the upper and lower surfaces with LED (light emitting diode) light-curing unit (n=10). Experimental 3D printing dental resins were prepared, to which two photoinitiators were added. Digital light processing type 3D printer (EMBER, Autodesk, CA, USA) was used for 3D printing. The specimen size was 64 mm×10 mm×3.3 mm according to ISO 20795-1. The final specimens were tested for flexural strength and flexural modulus, and MTT test was performed. Furthermore, one-way analysis of variance was performed, and the post-test was analyzed by Duncan’s test at α=0.05. Results: The flexural strength of both Bis-GMA+CQ (97.12±6.47 MPa) and UDMA+TPO (97.40± 3.75 MPa) was significantly higher (p<0.05) in the experimental group. The flexural modulus in the experimental group of UDMA+TPO (2.56±0.06 GPa) was the highest (p<0.05). MTT test revealed that all the experimental groups showed more than 70% cell activity. Conclusion: The composition of UDMA+TPO showed excellent results in flexural strength, flexural modulus, and biocompatibility.
목차
INTRODUCTION
MATERIALS AND METHODS
1. 레진 시편 제작
2. 기계적 성질(굴곡강도와 굴곡계수)
3. 생물학적 성질(MTT test)
4. 통계분석
RESULTS
1. 기계적 성질
2. 생물학적 성질(MTT test)
DISCUSSION
CONCLUSIONS
CONFLICT OF INTEREST
ORCID
REFERENCES