Recently, radiation shielding sheets made of eco-friendly materials have been widely used in medical institutions. The shielding sheet is processed into a solid form by thermoforming by mixing a shielding material with a polymer material. The base is resin-based and has a limit in tensile strength, and for this purpose, fibers such as non-woven fabrics are used on the surface. The shielding sheet process technology has a problem in that the tensile strength rapidly decreases when the content of the shielding material is increased to increase the shielding performance. In order to improve this, this study intends to compare and evaluate the method of laminating and coating the fibers in the sheet process. In comparison of the three types of sheets, there was no difference in shielding performance between the fiber-coated sheet and the compression sheet, but there was a large difference in tensile strength.

한국어

최근 의료기관에서 친환경 재료로 제작된 방사선 차폐시트를 많이 사용하고 있다. 차폐시트는 폴리머 소재에 차폐물질을 혼입하여 열성형으로 고형적인 형태로 가공된다. 베이스는 수지 계열로 인장강도에는 한계가 있으며, 이를 위해 표면에 부직포 등의 섬유를 합포하여 사용하고 있다. 차폐시트 공정 기술은 차폐성능을 높이고자 차폐물질의 함유 량을 높이면 인장강도가 급격히 떨어지는 문제점을 제시하고 있다. 이를 개선하고자 본 연구에서는 차폐시트에 섬유를 Binding하는 방식과 부직포에 소량의 차폐물질인 텅스텐을 함유하여 적층구조로 Laminating방식을 기본 폴리머 형태 로 Compression molding방식 세 가지 종류의 차폐시트를 제조하여 동일한 차폐 물질량을 기준으로 차폐성능과 인장 강도를 비교 평가하였다. 세 종류 차폐시트의 비교에서 섬유 코팅 시트와 압착 방식의 시트는 차폐성능 차이는 5%정도 이며, 인장강도는 65MPa에서 280MPa로 큰 차이가 나타났다. 적층구조의 차폐시트는 차폐 성능도 차이가 있었으며, 인장강도도 기준의 4배로 증가하였다.