Polymethyl methacrylate (PMMA), a self-curing resin mainly used in removable orthodontic appliances, is an acrylic resin mainly used in the field of modern dentistry. As an advantage, it has been used for a long time as a material for orthodontic devices in dentistry due to its color and volume, tissue affinity, and stability. The production of PMMA can be divided into self-polymerization method and thermal polymerization method according to activation method. Self-curing resins have long been used as orthodontic devices. The resin injection method is largely divided into a sprinkle-on method and a mixing method. In this study, we intend to test the mechanical properties according to the resin injection method of the orthodontic device, such as strength, modulus of elasticity, and surface roughness. There was no significant difference in strength as a result of three-point bending strength test on rectangular specimens (1.4 × 3.0 × 19.0 mm) of orthodontic PMMA. There was also no significant difference in hardness. There was no significant difference in surface roughness. It was confirmed that the orthodontic PMMA had no significant difference in mechanical properties according to the resin injection method of the orthodontic device.

한국어

가철성 교정장치에서 주로 사용하고 있는 자가중합 레진인 Polymethyl methacrylate (PMMA)는 현대 치의학 분야에서 주로 쓰이고 있는 아크릴릭 레진이다. 장점으로 색과 체적의 조직 친화성,안정성 등 있어 치과에선 교정장치 재료로 오랫동안 사용해 왔다. PMMA의 제작은 활성화 방법에 따라 자가중합방식과 열중합 방식으로 나눌 수 있다. 자가중합 레진은 치과 교정장치로 오래동안 사용되고 있다. 레진의 주입방법은 크게 적층법(sprinkle-on method)와 혼합법(mixing method)이 있다. 본 연구에서는 교정장치의 레진 주입방법에 따른 기계적 특성인 강도, 탄성계수 경도, 표면조도를 실험 해보고자 한다. Orthodontic PMMA 의 직사각형 시편 (1.4×3.0×19.0 mm)에 3점 굽힘강도 실험한 결과 강도에선 유의한 차이가 없었다. 경도 역시 유의한 차이가 없었다. 표면조도도 큰 차이가 보이지 않았다. Orthodontic PMMA는 교정용 장치의 레진주입 방식에 따른 기계적 특성의 유의한 차이가 없음을 확인하였다.