earticle

영어

This is a parameter study for the direct fabrication of a large grain YBCO bulk superconductors using Y2O3, BaCO3 and CuO powders without any grinding step. The cracks, which have been formed due to volume contraction during calcination step, have been prevented by controlling the heating rate at 930~950 ℃. It has been observed that multi-grain growth has occurred due to the dissolution of Sm123 seed due to the retention of carbon in Ba-Cu-O melt. In order to accelerate the carbon release in prior calcination heat treatment, the reduction of pellet thickness and the drilling of artificial holes have been applied. Single-grain YBCO bulk superconductor has been successfully fabricated by stacking multiple thin slab. However, the crack formation has been rather prominent for the compact with artificial holes. The use of buffer pellet, which is supposed to act as diffusion barrier, has prevented the dissolution of Sm123 seed crystal and has led to the growth of single grain of high content of carbon containing specimen.