Through the scientific analysis of the earthenware, pottery, and roof tile excavated from this study site, it was tried to identify the physical and chemical properties of the artifacts and the correlation between the excavated points. The color difference was different among samples due to the difference of firing temperature. In cross-sectional observation, the color difference between inside and outside was clearly distinguished due to the thickness of the wall. Absorption rate was very low at less than 5% in YI-1 and YI-3, and the other samples were higher than that, but these values are similar to those of ordinary earthenware. In the mineral analysis, some of the mullite was detected, and the minerals of the spinel group were also identified. Therefore, it is estimated that four samples were fired at a temperature of about 1100℃, but YI-5 was fired at 1000℃ or less due to the detection of muscovite. As a result of examining the correlation between the samples, the values of magnetic Susceptibility were varied in all samples, but the ranges of values were not large. Additionally the statistical analysis using the principal element and trace element content, it was difficult to distinguish between samples. In conclusion, it is estimated that all the samples are similar to each other in terms of raw materials between building and kiln points.

한국어

용인 덕성리 지구에서 발굴된 토기와 도기, 기와 등 5점에 대한 자연과학적 분석 을 통해 기물의 물리화학적 특성을 파악하고, 출토 유구 간의 상관성을 파악하고자 하였다. 색차는 소성온도의 차이로 인하여 시료 간에 차이를 보이며, 단면관찰에서 는 기벽의 두께로 인하여 내부와 외부의 색상 차이가 확실히 구분된다. 흡수율은 YI-1번과 YI-3번은 5% 이하로 매우 낮았으며, 다른 시료들은 일반적인 토기의 흡수 율에 해당된다. 구성 광물분석에서는 일부는 물라이트가 검출되었고, 스피넬군의 광물도 확인되어 1,100℃ 정도의 온도에서 소성되었을 것으로 보이며, YI-5번 시료 는 백운모가 검출되어 1,000℃ 이하에서 소성되었을 것으로 추정된다. 원료의 상관 성을 살펴본 결과, 전암대자율 값은 0.16∼4.25까지 모든 시료에서 다양한 값을 보 였으나 값의 범위가 넓지 않았고, 주요성분 원소와 미량원소 함량을 이용한 통계분석에서 시료 간의 구별이 어려웠다. 이는 건물지나 가마 출토편들 간의 원재료적인 측면에서 모든 시료들이 서로 유사한 것으로 판단된다.