영어

The volatile organic compounds(VOCs) have been recognized as major contributor to air pollution. The catalytic oxidation is one of the most important processes for VOCs destruction due to getting high efficiency at low temperature.
In this study, monometallic Pt and bimetallic Pt-Ru, Pt-Ir were supported to γ-Al2O3. In order to
distribute metals uniformly, H2O-H2 treatment method was used. Xylene, toluene and MEK were used as reactants. The monometallic or bimetallic catalysts were prepared by the excess wetness impregnation method and were characterized by XRD, XPS,and TEM analysis.
In the VOCs oxidation, Pt-Ru, Pt-Ir bimetallic catalyst had multipoint active sites, so it improved the range of Pt metal state. Therefore, bimetallic catalysts were higher conversion of VOCs than
monometallic ones. The effect of H2O-H2 treatment was uniform distribution of Pt particles.
In this study, the use of small amount of Ru, Ir to Pt promoted oxidation conversion of VOCs. In
addition to, H2O-H2 treatment promoted oxidation conversion of VOCs on the γ-Al2O3 support.

한국어

VOC는 대기오염의 주원인으로서 인식되어왔다. 촉매산화는 저온에서 높은 효율을 나타내기 때문에 VOCs 제거를 위한 가장 중요한 처리기술중 하나이다. 본 연구에서는 γ-Al2O3 담체에 Pt, Pt-Ru 그리고 Pt-Ir을 담지 시켜 촉매를 제조하였다. 금속 분산에 따르면 H2O-H2 처리방법이 사용되었고, 반응물로서 xylene, toluene 그리고 MEK를 사용하였다. 단일 또는 두 가지 이상의 촉매들은 함침법에 의해 준비하였고, XRD, XPS, TEM 분석을 통하여 특성화하였다.　
VOCs산화에서, Pt-Ru, Pt-Ir 촉매는 다양한 활성점을 나타내었고 그것은 Pt의 metal 영역를 강화시켰다. 따라서 두 가지 금속으로 이루어진 촉매가 단일 금속으로 이루어진 촉매에 비해 VOCs 전환율이 더 높았다. H2O-H2 처리는 Pt 입자의 분산에서 형태에 영향을 미쳤다.
본 연구에서 Pt에 소량의 Ru, Ir 첨가는 VOCs의 산화반응을 증진시켰고, γ-Al2O3 담체상에서 H2O-H2 처리는 VOCs의 산화반응을 증진시켰다.