This study is to analyze and compare ABA’s (Alum Based Adsorbent) arsenic adsorption efficiency in terms of changes of forms of arsenic, solid and liquid ration, pH, reaction time, etc. Two types of ABA using alum sludge, which is a byproduct obtained from the water treatment system, was used in this experiments. The one was dried at 105oC for 24 hours, and the other one was created through calcination process at 600oC for 6 hours. Pentavalent aresenical is higher than trivalent aresenical in ABA’s arsenic adsorption efficiency. Arsenic adsorption efficiency of calcinated ABA at 500oC is 9.5 mg/g which is almost two times higher than 5.1 mg/g of dried ABA. Arsenic adsorption efficiency of calcinated ABA according pH is higher than dried ABA in all range and therefore, it is turned out that as the more organic carbon is on the surface of ABA, arsenic adsorption is more hindered. Hence, if organic carbon is removed by high temperature, ABA’s adsorption efficiency will be considerably improved.

한국어

본 연구는 비소로 오염된 물을 흡착 제거하기 위해 정수처리장의 침전 부산물인 alum sludge를 활용하여 제작한 ABA (Alum Based Adsorbent)를 105oC에서 24시간 동안 건조한 ABA와 500oC에서 6시간 동안 소성하여 제조한 ABA로 구 분하여 비소의 존재형태별, 고액비, pH, 반응시간 등의 조건별 흡착실험을 비교 분석하였다. ABA의 비소 흡착효율은 5 가 비소가 3가 비소보다 큰 것으로 나타났으며, 500oC에서 소성하여 제조한 ABA의 흡착효율은 9.5 mg/g로 105oC에서 건조하여 제조한 ABA의 흡착효율 5.1 mg/g보다 약 2배 큰 것을 확인할 수 있었고, pH별 흡착효율도 고열에서 소성한 ABA가 pH 전 구간에서 모두 증가하는 것으로 나타나 ABA 표면에 유기탄소가 많을수록 비소 흡착이 방해받는 것으로 확인할 수 있었다. 따라서, 고온으로 유기탄소를 제거함으로써 ABA의 흡착능이 크게 개선시킬 수 있을 것으로 판단된다.