In dental resin cement studies, viscosity is also an important factor in the adhesion of tooth defects and implants. This study used BisGMA and HPMA as the main ingredients, triethylene glycol dimethacrylate (TEGDMA) as a diluent, and benzoyl peroxide (BPO) as a photoinitiator. The physical properties of graphene oxide used as an additive for functionality were evaluated, and its use as a dental resin cement material was investigated.The rupture strength has the tendency to increase along with the increase of the ratio of graphene oxide that was added, which seemed to reflect the effect of the high strength property of graphene oxide. The flexural strength also has the tendency to increase when about 0.5% of graphene oxide was added the same as the increase of rupture strength.When graphene oxide was added, according to viscosity use, the utilization as high-quality dental resin cements will increase.
목차
1. Introduction
2. Experimental
2.1 Materials and Reagents
2.2 Experimental Method
2.3 Instruments and Analysis
2.4 Measuring Instruments and Analysis
3. Results and Discussions
3.1 Each Ref.
3.2 Effects of Graphene Oxide
4. Conclusions
References