The EMI shielding effectiveness of shielding layers thickness was analyzed when the low conductivity shielding layers was placed in the near field of the noise source. A spiral antenna with broadband characteristics was used as the noise source, and graphite was selected as the low conductivity shielding material. Two spiral antennas were constructed to analyze the transmission coefficient between two antennas, and the distances between the transmitting and receiving antennas were 5 cm and 10 cm. The thickness of the shielding layers was changed from 1 um to 200 um. The frequency was changed from 100 MHz to 6 GHz to obtain a maximum SE(Shielding Effectiveness) of 70 dB. In this simulation, electronic shielding was used due to the nature of graphite, which is a shielding film material. Based on these results, we will study how to improve the shielding performance by implementing magnetic shielding in the future.

한국어

노이즈 소스의 근거리장에 저전도율 차폐막이 놓여있을 때 차폐막 두께에 따른 EMI 차폐효과를 분석하였다. 노이즈 소스로는 광대역 특성을 갖는 나선형 안테나를 이용하였으며, 저전도율 차폐 재료로는 그래파이트를 선정하였다. 나선형 안 테나 두 개를 만들어 두 안테나 사이의 투과계수를 분석하였고, 송수신 안테나 사이의 거리는 5 cm와 10 cm인 두 경우에 대해 수행하였다. 차폐막의 두께는 1 um에서 200 um까지 변화시켰다. 주파수는 100 MHz에서 6 GHz까지 변화시켜 최대 70 dB의 SE(Shielding Effectiveness)를 얻었다. 본 시뮬레이션에서는 차폐막 재료인 그래파이트의 특성상 전기적 차폐 (electronic shielding)를 이용하였다. 이 결과를 바탕으로 향후 자기 차폐를 구현하여 차폐 성능을 향상시킬 수 있는 방법을 연구할 예정이다.