Resource and environmental problems are emerging due to rapid industrialization. As a result, although solar cells have developed and solved the above problem to a certain extent, the soil pollution problem caused by generation of waste solar cell modules has emerged due to the life of 15 to 20 years of the modules supplied since 1990. As the generation of waste solar cell module is expected to increase, a study on the recovery of silicon from the waste solar cell module was carried out. The solar cell module is composed of silver (Ag), silicon (Si) and aluminum (Al). Phosphoric acid and nitric acid were used to recover silicon (Si). The removal ratio of Al from the solar cell was 99.99% using 2 M phosphoric acid at 100oC. In case of Ag, the removal ratio was 99.99% using 2 M nitric acid at 40oC. We also analyzed the purity of valuable metals (Al, Ag) and silicon (Si) using Energy Dispersive X-ray Spectroscopy (EDS) and Inductively Coupled Plasma (ICP).

한국어

최근 급속한 산업화로 인하여 자원 문제와 환경문제가 대두되고 있다. 이에 따라 태양전지가 발달하여 위의 문제를 어 느 정도 해결하였지만, 1990년도부터 보급된 모듈이 15~20년의 수명으로 인하여 현재 폐 태양전지모듈 발생으로 인한 토양오염 문제가 급부상하고 있다. 폐 태양전지 모듈 발생량이 증가할 것으로 예상됨에 따라 폐 태양전지 모듈로부터 실 리콘 회수에 관한 연구를 수행하였다. 태양전지 모듈은 은(Ag), 실리콘(Si), 알루미늄(Al) 등으로 이루어져 있다. 태양전 지로부터 실리콘(Si)을 회수하기 위해서 인산과 질산을 사용하였으며, 100oC에서 2 M의 인산을 이용하여 99.99%의 Al 을 제거할 수 있었으며, Ag의 경우 40oC에서 2 M의 질산을 이용하여 99.99% 제거할 수 있었다. 또한, EDS(Energydispersive X-ray spectroscopy)와 ICP(Inductively Coupled Plasma)를 이용하여 유가금속(Al, Ag)과 실리콘(Si)의 순도 를 분석하였다.