earticle

영어

Shielding effectiveness (SE) improvement with EMI shield layers fabricated by conformal spray coating system was studied. Silver or Nickel powder filled acrylic resin were sprayed on the samples. We compared the performance with the viscosity of 400 cPs and 100 cPs cases. The thickness range of the coating layer was 20 to 50 um for the silver, 60 to 120 um for the nickel. The shielding effectiveness was measured by ASTM D4935 using coaxial type TEM-cell. The silver-filled resin showed much better performance than that of the nickel-filled resin. The shielding effectiveness increased almost proportional to the thickness of the coating layers until being saturated around 63 dB for the silver-layer or around 34 dB for the nickel-layer. The best performance measured in this study was the shielding effectiveness of 63 dB with 35 μm-thick of silver-layer.

한국어

콘포멀 스프레이 코팅으로 형성한 EMI 차단막으로 차폐효과(SE)를 얼마나 개선할 수 있는지 연구하였다. 차단막을 형성하는데 사용한 재료는 도체 분말을 아크릴계 바인더에 혼합한 금속-레진 복합재료이며, 금속분말로는 은(Ag)과 니켈 (Ni)을 비교하였다. 재료의 점도는 400 cPs와 100 cPs에서 차폐성능을 비교하였다. 차단막의 두께는, 은의 경우 20 um에서 50 um, 니켈의 경우 60 um에서 120 um로 만들어 비교하였다. 차폐효과의 측정은 동축형 표준 측정기를 이용하여 ASTM D4935 방법으로 수행하였다. 니켈 시료보다 은 시료의 차폐효과가 우수했다. 차폐효과는 차단막 두께와 비례해 증가하지만 35 um 이상에서 더 이상 증가하지 않는다는 사실도 관찰하였다. 가장 차폐효과가 좋은 경우는 35 um 두께 은 시료 차단막으 로, 63 dB의 차폐효과가 측정되었다.