earticle

영어

The steel has been used in modern industry, car maker and electric appliance. The steel have some problem, specially corrosion problem. To solve corrosion problem, Zn electrodeposit on steel have been adapted. Recently, The modern industry asks to increase corrosion resistance. Naturally, Increasing corrosion resistance increases the thickness of Zn electrodeposit. But increasing thickness of Zn electrodeposit has some problems. In making part, There are some crack. This crack cause to decrease corrosion resistance. To solve this problem, it is interested in Zn Based alloy electrodeposit such as Zn-Cr. Here, the influence of the electrolytic conditions on the composition of the alloy plating in the chloride bath was investigated. The results are explained by the cathode overvoltage curve of Cr and Zn. As the current density of the cathode increases, Zn content of electrodeposit decrease and Cr content of electrodeposit increase. As the temperature of the electrolyte increases, Zn content of electrodeposit decrease and Cr content of electrodeposit increase.

한국어

강은 자동차 제조업체 및 전기 제품에 많이 사용되고 있으나 부식으로 많은 문제점이 발생한다. 이러한 부식문제를 해결하기 위해 강 위에 아연전기도금을 두껍게 하고 있다. 그러나 아연 도금의 두께가 두꺼워지면 부품 제조 시 크렉이 발생하기 쉬우며, 이로 인해 부식이 더욱더 악화될 수 있다. 이러한 부식 문제를 해결하기 위해 아연과 크롬합금도금에 관심이 집중되고 있다. 본 연구에서는 염화욕에서 합금도금의 조성에 미치는 전해조건의 영향을 조사하였다. 전류밀도가 증가함에 따라 Zn함량이 감소하고 Cr함량은 증가하였다. 전해액 온도가 증가함에 따라 Zn함량이 감소하고 Cr함량은 증가하였으며, 그 결과는 음극 분극곡선으로 가지고 해석되었다.