The metal oxide/graphene nanocomposites are promising functional materials for high capacitive electrode material of secondary batteries, and high sensitive material of high performance gas sensors. In this study, vanadium dioxide(VO2) nanostructrures were grown on CVD graphene which was synthesized on Cu foil by thermal CVD, and exfoliated graphene which was exfoliated from highly oriented pyrolytic graphite(HOPG) using a vapor transport method. As results, VO2 nanostructures on CVD graphene were grown preferential growth on abundant functional groups of graphene grain boundaries. The functional groups are served to nucleation site of VO2 nanostructures. On the other hand, 2D & 3D VO2 nanostructures were grown on exfoliated graphene due to uniformly distributed functional groups on exfoliated graphene surface. The characteristics of morphology controlled growth of VO2/graphene nanocomposites would be applied to fabrication process for high capacitive electrode materials of secondary batteries, and high sensitive materials of gas sensors.

한국어

금속 산화물/그래핀 형태의 복합 나노소재는 높은 전기용량을 갖는 2차 전지의 전극용 소재 또는 고감도 가스 센서의 감지물질 등으로 활용되는 매우 유용한 기능성 소재이다. 본 논문에서는 열 화학기상증착(CVD, Chemical Vapor Deposition)으로 Cu Foil 위에 대면적으로 합성된 CVD 그래핀 및 고정렬 열분해 흑연(HOPG, Highly Oriented Pyrolytic Graphite)으로부터 기계적으로 박리된 그래핀 기판 위에 이산화바나듐(VO2) 나노구조물을 기상수송방법으로 직접 성장시키는 연구를 수행하였다. 연구결과 CVD 그래핀 기판의 경우, 그래핀 결정 경계에서 상대적으로 많이 존재하는 기능기들이 VO2 나노구조물에서 핵형성의 씨앗으로 작용하는 것이 확인되었다. 반면에 HOPG에서 기계적으로 박리된 그래핀 나노시트 표면에는 기능기가 균일하게 분포하기 때문에, 2차원과 3차원 형태로 VO2 나노구조물이 성장되었다. 이러한 연구결과는 고기능성 VO2/그래핀 나노복합소재를 이용하여 높은 전기용량을 갖는 2차 전지 전극소재 및 고감도 가스 센서의 감지물질 합성에 유용하게 활용될 것으로 전망된다.