This study examined the condition of degraded plastic artifacts and conducted materials assessments for conservation treatment. The properties and bond characteristics of five types of adhesives(EVA, PVAc, Cyanoacrylate) were evaluated to select the adhesive most suitable for conservation treatment. The degradation of plastic artifacts caused cracks, peelings, and surface warping. According to the FT-IR analysis, the synthetic resin used in the artifact was estimated to EVA type. The properties of the adhesives were evaluated through acidity, and hardness measurements. The results showed that acidity varies with the type of adhesive, and that the hardness of PVAc was higher than those of EVA. On comparing the bond characteristics of the samples after artificial degradation, it was found that PVAc and Cyanoacrylate increased the chromaticity and hardness of the samples, while EVA was the most stable with relatively little change. Thus, EVA was confirmed to be the most suitable materials for conservation treatment of degraded plastic artifacts. In this study, as the experiment of treatment materials based on actual artifact, it is expected that it could be used a basis research for conservation treatment of plastic artifacts.

한국어

본 연구는 열화된 플라스틱 작품의 보존처리를 위해 작품의 상태조사 및 재질분석을 실시하였으며, 보존처리에 주로 사용되는 접착제 5종(EVA계, PVAc계, Cyanoacrylate계)의 물성 및 접합특성을 평가하여 작품에 적합한 접착제를 선정하고자 하였다. 작품은 현재 열화로 인해 표면의 균열, 들뜸, 형태적 변형이 발생하였으며, FT-IR을 통한 재질분석 결과, 작품에 사용된 합성수지는 EVA계로 추정되었다. 접착제의 물성평가를 위해 산성도 및 경도 측정을 실시한 결과, 산성도는 접착제 종류에 따라 다르게 나타났으며, 경도는 EVA계 보다 PVAc계 접착제가 더 높게 측정되었다. 의사시편 을 제작하여 인공열화 후 접합특성을 비교한 결과, PVAc, Cyanoacrylate계 접착제는 색차 및 경도가 크게 증가하는 모습을 보인 반면 EVA계 접착제는 변화가 적어 가장 안정하였다. 작품의 보존처리 재료로써 EVA계 접착제가 가장 적합한 것으로 나타났다. 본 연구는 실제 작품을 대상으로 실시한 처리재료 연구로써 현재 플라스틱 작품의 보존처리에 대한 국내 연구가 부족한 상황에서 기초 자료로 활용 가능할 것으로 기대된다.