치과용 지르코니아 이장재 처리에 따른 지르코니아와 도재의 전단결합강도 비교

원문정보

Shear bond strength of a layered zirconia and porcelain according to treatment of zirconia liner

서정일, 박원욱, 김양근

피인용수 : 0(자료제공 : 네이버학술정보)

초록

영어

Purpose: Physical and chemical properties of gold is most suitable to be restored of teeth to its original state. Recently zirconia was used instead of gold because of esthetical and intimacy of human body. Because of high strength and high abrasion resistance of zirconia, all zirconia artificial tooth lead to wear the original tooth of opposite site. To preserve this original tooth, zirconia artificial tooth covered with dental ceramic glass was used. When joining the zirconia core and dental ceramic glass, difference of their thermal expansion coefficient and wetting ability is generated the residual stress at interface lead to crack. In order to solve this problem, intermediate layer what is called zir-liner was imported to decrease the residual stress and increase the bonding strength. Methods: In this study, to identify the optimum conditions for manufacturing process, various methods to rough the surface of zirconia core were adopted, and vary the thickness of interlayer, and analyzed bond strength. Results: Bond strength of sanding specimens group showed higher than that of non-sanding specimens group, and once applied intermediate layer with sanding specimens showed highest bond strength with 28 MPa. SEM photomicrographs of zirconia cores fired at 1500℃ showed parallel straight lines in sanding and pockmarked surface in blasting surfaces as abrasion traces. Observation of the destruction section after shear test by SEM were carried out. Liner applied non-sanding group and non-liner applied sanding group all showed interfacial crack. Sandblasting group with non-liner showed remained dental ceramic glass on the surface of zirconia. Sandblasting group with once applied liner showed partially remained liner and dental ceramic glass on the surface of zirconia. XRD analysis revealed that sandblasting group showed higher monoclinic peaks than other specimens group and this result was due to the high collision energy for stress induced phase transformation. Conclusions: A study on the improvement of bonding strength between zirconia and dental ceramic glass steadily carried out for the future to practical use.

목차

[Abstract]
 Ⅰ. 서론
 Ⅱ. 연구 방법
  1. 실험 순서
  2. 지르코니아 시편 제작
  3. 시편의 소성
  4. 전단결합 강도 측정
  5. 미세구조 관찰
  6. XRD 관찰
 Ⅲ. 결과
  1. 초기시편 표면 관찰
  2. 전단강도 측정
  3. 파단면의 미세구조 관찰
  4. 절단면의 미세구조 관찰
  5. 표면 X-선 회절분석
 Ⅳ. 고찰
 Ⅴ. 결론
 REFERENCES

저자정보

  • 서정일 Jeong Il Seo. 진주보건대학교 치기공과
  • 박원욱 Won Uk Park. 진주보건대학교 치기공과
  • 김양근 Yang Geun Kim. 진주보건대학교 치기공과

참고문헌

자료제공 : 네이버학술정보

    함께 이용한 논문

      ※ 기관로그인 시 무료 이용이 가능합니다.

      • 4,000원

      0개의 논문이 장바구니에 담겼습니다.