Evaluation of Flexural strength and surface porosity of three indirect composite resins
초록
영어
Purpose: The purpose of this study was to evaluate flexural strength, composite surface and fractured surface of three different indirect composite resins. Methods: Fifteen bar-shaped specimens (25mm x 2mm x 2mm) were fabricated for each FL group (Flow type and Light curing) and PLP group (Putty type and Light, Pressure curing) and PL group (Putty type and Light curing) according to manufacturer’s instructions and ISO 10477. Fabricated specimens were stored in the distilled water for 24 hours at the temperature of 37℃. Three-point bending strength test was performed to measure flexural strength using universal testing machine at a crosshead speed of 1mm/min (ISO 10477). Surface and fractured surface of specimens were observed by digital microscope. Results were analyzed with Kruskal-wallis tests (α = 0.05). Results: Mean (SD) of three different indirect composite resins were 83.38 (6.67) MPa for FL group, 139.90(16.53) MPa for PLP group and 171.72(16.74) MPa for PL group. Flexural strength were statistically significant (p<0.05). Differences were not observed at fractured surface among three groups. However, many pores over 100㎛ were observed at PL group in observing surface of specimen. Conclusion: Flexural strength of composite resins was affected by second polymerization method and content of inorganic filler.
목차
Ⅰ. 서론
Ⅱ. 연구 방법
1. 연구재료
2. 시편제작
3. 굴곡강도의 측정
4. 파절면 및 표면 관찰
5. 통계분석
Ⅲ. 결과
1. 굴곡강도
2. 표면관찰
Ⅳ. 고찰
Ⅴ. 결론
REFERENCES